AbstractCorrosion performance of NiCr and NiCrBSi coatings produced by APS, HVOF, and HVAF was studied by electrochemical measurements and immersion tests in 0.5 and 3.5 wt.% NaCl solutions. In the electrochemical measurements, the NiCr coatings performed better than the NiCrBSi coatings. The effect of the coating process on the corrosion resistance of the material was significantly lower than that of the selected materials, NiCr or NiCrBSi. All the coatings showed a tendency to passivate but suffered from localized corrosion. During immersion exposure for ten weeks, localized corrosion appeared at heterogeneous areas of the coatings, including voids, defects, or powder particles that had not melted during the spraying process.
Funder
Technical Research Centre of Finland
Publisher
Springer Science and Business Media LLC
Subject
Materials Chemistry,Surfaces, Coatings and Films,Condensed Matter Physics
Reference36 articles.
1. N. Papageorgiou, A. Von Bonin and N. Espallargas, Tribology International Tribocorrosion Mechanisms of NiCrMo-625 Alloy: An Electrochemical Modeling Approach, Tribiol. Int., 2014, 73, p 177-186. https://doi.org/10.1016/j.triboint.2014.01.018
2. L.N. Moskowitz, Application of HVOF Thermal Spraying to Solve Corrosion Problems in the Petroleum Industry-an Industrial Note, J. Therm. Spray Technol., 1993, 2(1), p 21-29.
3. A. Neville, T. Hodgkiess and J.T. Dallas, A Study of the Erosion-Corrosion Behaviour of Engineering Steels for Marine Pumping Applications, Wear, 1995, 187, p 497-507.
4. A. Neville, J.M. Perry, T. Hodgkiess and H.P. Chua, Wrought and High-Velocity Oxy Fuel Sprayed Inconel 625—Examination of Corrosion Aspects, Proc. Inst. Mech. Eng., 2000, 214(1), p 41-48.
5. S. Shrestha, A. Sturgeon, T. Hodgkiess and A. Neville, Corrosion Behaviour of High Velocity Oxy-Fuel (HVOF) Sprayed Ni-Cr-Si-B Coatings, Thermal Spray 2002. E. Lugscheider Ed., DVS, Essen, 2002
Cited by
9 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献