Author:
Raumel Selina,Barienti Khemais,Luu Hoang-Thien,Merkert Nina,Dencker Folke,Nürnberger Florian,Maier Hans Jürgen,Wurz Marc Christopher
Abstract
AbstractEngineering in vacuum or under a protective atmosphere permits the production of materials, wherever the absence of oxygen is an essential demand for a successful processing. However, very few studies have provided quantitative evidence of the effect of oxidized surfaces to tribological properties. In the current study on 99.99% pure copper, it is revealed that tribo-oxidation and the resulting increased abrasive wear can be suppressed by processing in an extreme high vacuum (XHV) adequate environment. The XHV adequate atmosphere was realized by using a silane-doped shielding gas (1.5 vol% SiH4 in argon). To analyse the influence of the ambient atmosphere on the tribological and mechanical properties, a ball—disk tribometer and a nanoindenter were used in air, argon, and silane-doped argon atmosphere for temperatures up to 800 °C. Resistance measurements of the resulting coatings were carried out. To characterize the microstructures and the chemical compositions of the samples, the scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD) were used. The investigations have revealed a formation of η-Cu3Si in silane-doped atmosphere at 300 °C, as well as various intermediate stages of copper silicides. At temperatures above 300 °C, the formation of γ-Cu5Si were detected. The formation was linked to an increase in hardness from 1.95 to 5.44 GPa, while the Young’s modulus increased by 46% to 178 GPa, with the significant reduction of the wear volume by a factor of 4.5 and the suppression of further oxidation and susceptibility of chemical wear. In addition, the relevant diffusion processes were identified using molecular dynamics (MD) simulations.
Publisher
Springer Science and Business Media LLC
Subject
Surfaces, Coatings and Films,Mechanical Engineering
Reference78 articles.
1. Bennett C. Meeting future copper demand. Available on https://copperalliance.org/resource/meeting-future-copper-demand/, 2019.
2. Mrowec S, Stoklosa A. Oxidation of copper at high temperatures. Oxid Met 3(3): 291–311 (1971)
3. Ph.D. Thesis;S W Hymes,1999
4. Bowden F P, Tabor D. The Friction and Lubrication of Solids. Oxford (UK): Clarendon Press, 1986.
5. Kragelski I W. Reibung und Verschleiss. München (Germany): Hanser, 1971. (in German)
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献