Self-lubricating triboactive (Cr,Al)N+Mo:S coatings for fluid-free applications

Abstract

AbstractWithin this study, self-lubricating and triboactive (Cr,Al)N+Mo:S coatings were developed and investigated for the deposition on components in a low-temperature physical vapor deposition (PVD) hybrid process. Therefore, direct current magnetron sputtering (dcMS) and high power pulse magnetron sputtering (HPPMS) PVD were combined by using an industrial coating machine. Hereby, it was possible to deposit dense and smooth triboactive, self-lubricating nitride coatings with different chemical compositions and architectures on 16MnCr5E samples. Two coating architectures, a matrix monolayer and a graded coating structure, were developed to evaluate the effect on the tribological behavior. The morphology and coating thickness were analyzed by means of scanning electron microscopy (SEM). Furthermore, the indentation hardness and modulus of indentation as well as the compound adhesion between substrate materials and coating were analyzed. Tribological analyses of (Cr,Al)N+Mo:S-coated and uncoated samples were conducted under fluid-free friction regime at room temperature T = (20 ± 3) °C, a velocity v = 0.1 m/s and a distance s = 1000 m by varying the Hertzian contact pressure from 400 MPa ≤ pH ≤ 1300 MPa against steel counterparts, 100Cr6, in a pin-on-disk (PoD) tribometer. The graded coating architecture of (Cr,Al)N+Mo:S enabled a significant wear and friction reduction. Furthermore, Raman analyses prove the formation of solid lubrication tribofilm containing MoS2, MoO3 MoO2 and MoxOy at the toplayer of a graded (Cr,Al)N+Mo:S coating, which are responsible for the improved tribological behavior.