AbstractExperiments were carried out to investigate the wetting behaviour of liquid tin on two different steel substrates EN1.4301 stainless steel and 42CrMo4 low-alloyed steel. The experiments were carried out in a vacuum furnace at residual pressure (10−8 bar) with the temperature raised till 1233 K (960 °C). The transition of the liquid tin droplet from a non-wetting to a wetting state was achieved on the surface of both steels after the spontaneous oxide removal. The transition temperatures in the Sn/EN1.4301 and Sn/42CrMo4 systems were nearly identical, 1140 K and 1130 K, respectively. SEM images showed the formation of the Fe–Sn intermetallic compounds at the Sn/steel interfaces above the transition temperature. Tin penetration into the grain boundaries of EN1.4301 and 42CrMo4 steels was also observed.