Failure of a Secondary Superheater Tube in a 140-MW Thermal Power Plant-Reference-Cited by-同舟云学术

Failure of a Secondary Superheater Tube in a 140-MW Thermal Power Plant

Published:2013-12-04 Issue:1 Volume:14 Page:10-12
ISSN:1547-7029
Container-title:Journal of Failure Analysis and Prevention
language:en
Short-container-title:J Fail. Anal. and Preven.

Author:

Saha Atanu,Shukla A. K.

Publisher

Springer Science and Business Media LLC

Subject

Mechanical Engineering,Mechanics of Materials,Safety, Risk, Reliability and Quality,General Materials Science

Link

http://link.springer.com/content/pdf/10.1007/s11668-013-9773-3.pdf

Reference9 articles.

1. S.R. Paterson, T.W. Rettig. Remaining Life Estimation of Boiler Pressure Parts 2.25 Cr-1Mo Superheater and Reheater tubes. Project RP2253-5, Final Report, (Electric Power Research Institute, Palo Alto, 1987)

2. R. Viswanathan, J.R. Foulds, D.I. Roberts. Proceedings on Boiler Tube Failures in Fossil Power Plants, vol. 10 (EPRI, Palo Alto, 1987), pp. 3.35–53

3. R. Viswanathan, J.R. Foulds, Service experience, structural integrity, severe accidents and erosion in nuclear and fossil plants. ASME Press Vess. Pip. 303, 187–205 (1995)

4. R. Viswanathan, Damage Mechanisms and Life Assessment of High Temperature Components (ASM International, Metals Park, 1989)

5. M.C. Coleman, J.D. Parker, D.T. Welters, Behaviour of ferritic weldments in thick section Cr–Mo–V pipe at elevated temperatures. Int. J. Press. Vess. Pip. 18, 277–310 (1985)

Cited by 11 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Performance degradation analysis of a medium pressure superheater due to tube deactivation;Journal of Mechanical Engineering and Sciences;2023-06-28

2. Failure/Damage Mechanism of Boiler Tube;Springer Tracts in Mechanical Engineering;2023

3. Case Study VB: Dissimilar Metal Weld;Springer Tracts in Mechanical Engineering;2023

4. Failure Analysis of Heat Exchangers;Analysis and Prevention of Component and Equipment Failures;2021-08-30

5. Reducing the Risk of High Temperature Creep Failures in Refinery Service Component and Equipment;Journal of Pressure Vessel Technology;2019-08-02