Abstract
The development of antiferroelectric materials with large energy density and fast discharge speed makes dielectric capacitors possess great prospects for applications in pulsed power technology. Here, the PbHfO
3
-based ceramics with compositions of Pb(Hf
1-
x
Ti
x
)O
3
(PHT, 0.01 ≤
x
≤ 0.05) were synthesized, and their antiferroelectricity and phase transition behavior were studied. According to the tests of x-ray diffraction, dielectric spectrum, and polarization–electric field hysteresis loops, PHT ceramics gradually transition from an orthorhombic symmetric antiferroelectric phase to a hexagonal symmetric ferroelectric phase at room temperature as Ti
4+
concentration increases. The forward phase switching field of antiferroelectric to ferroelectric phase transition can be markedly regulated by the introduction of Ti
4+
, and the optimal energy storage performance was obtained in Pb(Hf
0.98
Ti
0.02
)O
3
ceramics with a large recoverable energy storage density of
W
rec
~ 4.15 J/cm
3
and efficiency of
η
~ 65.3% only at a low electric field of 190 kV/cm. Furthermore, the outstanding charge–discharge properties with an ultrafast discharge time (71 ns), remarkable discharged energy density (2.84 J/cm
3
), impressive current density (1,190 A/cm
2
), and ultrahigh power density (101 MW/cm
3
) at a low electric field of 170 kV/cm were obtained in studied ceramics. The excellent energy storage performance of PHT ceramics provides a promising platform for the application of dielectric capacitors.
Publisher
American Association for the Advancement of Science (AAAS)
Subject
Energy (miscellaneous),Fuel Technology,Materials Science (miscellaneous),Renewable Energy, Sustainability and the Environment
Cited by
9 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献