1. Materials and Processes Laboratory, Large Steam Turbine-Generator Department, General Electric Co., Schenectady, N. Y.
Abstract
The rates of fatigue crack propagation in several heat-treated steels were determined for several alloy steels heat-treated to yield strengths in the range 70,000 to 125,000 psi. For one steel crack growth rates were determined for both a thick notch bend specimen and for thin notched plate specimens. It is observed that the concepts of Griffith-Irwin fracture mechanics successfully correlate crack growth rates in the various geometry and thicknesses employed. However, the specific relationship is dependent on yield strength level. Microscopic examination suggests in some instances that inclusion segregates act effectively to locally accelerate crack growth rates.
Cited by
19 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献
1. Environmental Crack Growth Behavior Affected by Thickness/Geometry Constraint;Metallurgical and Materials Transactions A;2012-11-13
2. 1967;Bibliography on the Fatigue of Materials, Components and Structures;1990
3. Effect of specimen size on fatigue crack growth rate in AISI 4340 steel;Engineering Fracture Mechanics;1985-01
4. Fatigue crack growth in thin section type 316 stainless steel;Engineering Fracture Mechanics;1984-01
5. Zum Größeneinfluß im Low-Cycle Fatigue Bereich;Materialwissenschaft und Werkstofftechnik;1982-07