Experimental Investigation of Constraint Effects on Creep Crack Growth

Abstract

In this work the effects of specimen size and type on creep crack growth rates in stainless steel are examined. Experiments have been carried out on high constraint compact tension specimens (CT) and low constraint centre cracked panels (CCP) of ex-service 316H stainless steel. All testing was carried out at 550°C. Constraint effects have been observed in the data, with the large CT specimens having the fastest crack growth rate and the small CCP specimens the slowest. These trends are consistent with those that would be predicted from two parameter (C*–Q) theories. However, it is found that a constraint dependent creep crack growth model based on ductility exhaustion overpredicts the constraint dependence of the crack growth data.