In view of the near-tip constraint effect imposed by the geometry and loading configuration, a creep fracture analysis based on C* only is generally not sufficient. This paper presents a formulation of higher-order crack-tip fields in steady power-law creeping solids which can be derived from an asymptotic development of near-tip fields analogous to that of Sharma and Aravas and Yang et al. for elastoplastic bodies. The higher-order fields are controlled by a parameter named A2*, similar as in elastoplasticity, and a second loading parameter, σ∞. By means of the scaling properties for power-law materials, it is shown that A2* for a flat test specimen is independent of the loading level. Finally, we carry out small-strain finite element analyses of creep in single-edge notched tension, centered crack panel under tension, and single-edge notched bending specimens in order to determine the corresponding values of A2* for mode I cracks under plane-strain conditions. [S0021-8936(00)01202-2]
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics
Reference25 articles.
1. Williams, M. L.
, 1957, “On the Stress Distribution at the Base of a Stationary Crack,” ASME J. Appl. Mech., 24, pp. 111–114.
2. Li, Y., and Wang, Z., 1986, “Higher Order Asymptotic Field of Tensile Plane Strain Nonlinear Crack Problem,” Sci. Sin. (Series A), 29, pp. 941–955.
3. Betego´n, C., and Hancock, J. W., 1991, “Two-Parameter Characterization of Elastic-Plastic Crack-Tip Fields,” ASME J. Appl. Mech., 58, pp. 104–110.
4. D’Dowd, N. P., and Shih, C. F., 1991, “Family of Crack-Tip Fields Characterized by a Triaxiality Parameter—I. Structures of Fields,” J. Mech. Phys. Solids, 39, pp. 989–1015.
5. Parks, D. M., 1992, “Advances in Characterization of Elastic-Plastic Crack-Tip Fields,” Topics in Fracture and Fatigue, A. S. Argon, ed., Springer-Verlag, New York, pp. 59–98.
Cited by
45 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献