Adhesion to Bovine Dentin-Surface Characterization

Abstract

X-ray photo-electron spectroscopy (XPS) and secondary ion mass spectrometry (SIMS) were used to characterize the dentin surface, to determine the effects of different pre-conditioning procedures on the elemental composition of the dentin surface, and to investigate the interaction between dentin and a dentin bonding agent (ScotchBond) by studying the changes in the elemental composition of dentin as a result of the interaction. Scanning electron microscopy (SEM) was used to characterize sample surface morphology, which was then correlated with surface elemental composition. The results showed that: (a) the elemental composition of the smear layer was similar to that of the underlying dentin; (b) cleaning with hydrogen-peroxide did not produce any modification in the elemental composition of the dentin surface; and (c) acid-etching led to an almost complete demineralization of the dentin, leaving behind an organic-rich surface. The results suggest that bonding systems that use acid-etching as a pre-conditioning procedure should be based on agents able to interact with the organic components of dentin, since bonding agents that rely on a chelation-to-calcium reaction are unlikely to be successful. The investigation of the interaction between the bonding agent and dentin led to a postulated adhesive-bonding reaction mechanism and suggested a partially cohesive failure in the bonding agent during fracturing of a dentin-bonding-agent-bonded assembly.