Investigating the wear resistance of high-chromium cast irons A532-class III-type A against high-energy abrasive particles

Author:

Hosseinreza Saeed1ORCID,Rastegari Habibollah2,Hosseinpour Mohammadreza3,Garmeh Behdad1

Affiliation:

1. Division of Research and Development, Isfahan Casting Industries Co. (ICI), Isfahan, Iran

2. Department of Mechanical and Materials Engineering, Birjand University of Technology, South Khorasan, Iran

3. Metallurgy Lab, Isfahan Casting Industries Co. (ICI), Isfahan, Iran

Abstract

Regarding the widespread use of high chromium cast irons in manufacturing various industrial and mineral-processing parts such as liners, slurry pumps, and grinding balls, increasing erosion resistance is the key factor to enhance their performance. This research investigated three different chemical compositions of high chromium irons (in the eutectic and hypoeutectic range). Austenite destabilization process was conducted at two temperatures of 1060°C and 970°C followed by air cooling and then tempering at the range of 250°C to 400°C for 4 h. Erosion and bending tests were carried out on samples with optimal heat treatment conditions. Results show that the hardness of specimens heat-treated at 970°C, and also the low-carbon hypoeutectic specimens destabilized at 1060°C, increased by increasing tempering temperature over 300°C, which can be related to the formation of a higher volume fraction of M23C6 carbides. The best erosion resistance was observed in the low-carbon hypoeutectic specimen destabilized at 1060°C and tempered at 300°C. In addition, samples with higher erosion resistance exhibit lower bending strength. Finally, it was found that the principal wear mechanism was the occurrence of plastic deformation, and detachment of carbides from the surface before having an effective role in reducing wear.

Publisher

SAGE Publications

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3