Affiliation:
1. Nonmetallic Materials Division Air Force Materials Laboratory Wright-Patterson AFB, Ohio 45433
2. University of Dayton Research Institute Dayton, Ohio 45469
Abstract
The paper presents results on the damage mechanisms in hard object impact and their effect on the residual tensile strength of unidirectional Boron/Aluminum and Borsic/Titanium composites. The ballistic tests were carried out with 0.177" steel spheres impacting at the center of centilever plates over a velocity range of 50 to 4000 ft/sec. The induced ballistic damage and the different failure modes are examined by radiography and SEM, and the post impact residual tensile strength and residual velocity after perforation are studied for both materials. The damage induced in Boron/Aluminum consists mainly of lateral and axial cracks causing large strength degradation, up to 50 percent of the initial strength. Borsic/Titanium, on the other hand, shows much better impact resistance and the ballistic damage consists of localized plastic de formation and formation of a sheared plug causing strength degradation of 20 percent of the initial strength, as is the case with homogeneous titan ium. An analytical model based on fracture mechanics can predict fairly well the damage size and the residual tensile strength. Ballistic limit velocity and residual velocity after perforation are shown to be predictable by a model developed for homogeneous metallic plates.
Subject
Materials Chemistry,Mechanical Engineering,Mechanics of Materials,Ceramics and Composites
Cited by
22 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献