Aluminum and copper deposition through the process of thermal flame spray on polypropylene-pine wood fiber composite filaments and their applications

Abstract

This paper presents a study about polypropylene-pine wood composites, both as filaments and products, coated with aluminum (Al) or copper (Cu), obtained through flame thermal spray process after subjecting the composites to thermal treatments in the second and third step of the study. Results revealed that a previous aluminum layer was needed in order to obtain copper coatings on the composites. The physical and mechanical properties of both metal coated composite filaments were also evaluated and compared with the uncoated composite filaments with and without heat treating these. Consequently, it was observed that the nature of the coating adhesion on the substrates was mechanical, and therefore abrasion blasting of filaments or the use of a higher wood fiber content in the composite improved the Al or Cu adhesion. Also, it was observed that extruded wood fiber/PP filaments should not be cooled in water because pieces might be molded directly once the moisture affects the metal coatings adhesion onto the substrates.