In this study, the fatigue behavior of 0.25 wt.% graphene nanoplatelets (GnPs) reinforced and unreinforced impact damaged basalt/epoxy composite pressure vessels (CPVs) was investigated. The CPVs were subjected to low-velocity impact (LVI) of 2.5 J, 5 J, 7.5 J, 10 J, 15 J, 20 J, and 25 J under internal pressure of 50 bar (hoop/axial prestresses: 98/49 MPa). Then, to detect fatigue life changes, fatigue tests were performed at load rates of 30% of ultimate hoop stress (σHS), where sweat damage occurred in the basalt/epoxy CPVs under alternating internal pressure. Considering the remaining fatigue life and formation of the damages in the CPVs for all impact energies, to investigate the fatigue behavior and GnPs effects of CPVs subjected to low-velocity impact, an impact value of 5 J was preferred. The 5 J impact damaged CPVs were subjected to fatigue cyclic following ASTM D 2992 at load rates of 20%, 25%, 30%, 35%, and 40% of the σHS. The fatigue life of damaged CPVs was compared by that of undamaged over S-N curves. As the impact energy increased, the impact damage area increased. The increased size of damage reduced the fatigue life of basalt/epoxy CPVs. At the fatigue load rates mentioned above, the GnPs improved the fatigue life of damaged basalt/epoxy CPVs by about 3.5, 3.2, 11.3, 2.4, and 5 times, respectively.
Funder
Selcuk University Scientific Research Projects
Subject
Materials Chemistry,Mechanical Engineering,Mechanics of Materials,Ceramics and Composites
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献