Synthesis and characterization of high-temperature resistant and thermally conductive magnetic PBI/Fe3O4 nanofibers

Abstract

In the present study, magnetite nanoparticles were added to an electrospinning solution of polyvinylidene fluoride (PVDF)/polybenzimidazole (PBI) polymers to prepare PBI/Fe3O4 nanofibers (NFs). The operating voltage of the electrospinning device was set to 15 kV, the distance between the needle and the plate was 10 cm, and the feed rate was set to 0.3 mL h−1. The microstructures of the as-prepared NFs were investigated by Fourier transform infrared spectrophotometry, atomic force microscopy, thermogravimetric analysis, and vibration sample magnetometry. Magnetite-doped PVDF/PBI NFs exhibited superior magnetism and saturation magnetization in the range of 1.5–5 emu g−1. It was observed that the thermal resistance of the fibers increased with the increasing amount of magnetic particles and nanocomposite fiber (NCF) 1 and NCF2 exhibited excellent thermal resistance up to 415°C and 450°C, respectively. The heat conduction coefficient of the fibers was measured at 4, 6, and 8 W. The thermal conductivity of the NFs increased with the increasing amount of magnetite nanoparticles, and the highest thermal conductivity coefficient for NCF2 (1.83 W mK−1) was measured at 4 W.