Composite nanofiber meshes of well-aligned polyacrylonitrile (PAN)/FeCo nanofibers containing nanoparticles (NPs) were successfully fabricated by a magnetic-field-assisted electrospinning technology, which was confirmed to be a favorable method for the preparation of aligned composite nanofibers in this article. Meanwhile, FeCo NPs, with a particle size of approximately 60 nm, were synthesized using a hydrothermal route. The nanocomposite fibers were prepared by an electrospun solution of PAN containing 0, 2, 4, and 6 wt% NPs. The as-spun nanofibers were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and vibrating sample magnetometer. Both the diameters and the degree of alignment of the composite nanofibers decreased with the increase in voltage and increased with the increase in FeCo content. The composite nanofibers exhibited superior ordered performance, with the highest alignment value being 97%. Due to the highly ordered alignment structures, the composite nanofiber meshes showed large anisotropic magnetic property. In particular, the saturation magnetization of the composite nanofiber films in the parallel and perpendicular directions of the fiber axis were 42 emu/g and 19.5 emu/g, respectively. Meanwhile, the remanence also exhibited distinction in different directions (parallel: 2.01 emu/g; perpendicular: 0.86 emu/g).
Funder
the natural science foundation for Young Scientists of ShanXi Province
Subject
Materials Chemistry,Organic Chemistry,Polymers and Plastics
Cited by
13 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献