Abstract
This study presents, for the first time, the mechanical behavior of API 5L pipeline steels X42, X52, X60, X70, X80, and X100 with external and internal corrosion defects as well as a combination of both defects that has been named external–internal corrosion defects. The conventional methods to predict failure pressure in corroded pipes, such as B31G, RSTRENG-1, SHELL, DNV-99, PCORRC, and FITNET FFS, have also been discussed in this article. In addition, pipeline failure pressure has been estimated using the finite element method, considering that it is the best approach to calculate actual failure pressure. The external and internal corrosion defect investigated in this research manifests as a rectangular shape with spherical ends at the edges. When the external–internal corrosion defect appears, failure pressure data decrease dramatically because of severe damage. This is due to the decrease in the ligament (effective area) caused by the corrosion defect. To have a good estimation of the pipeline failure pressure with an external–internal corrosion defect, DNV-99 method can be used with acceptable certainty.
Subject
Building and Construction,Civil and Structural Engineering
Cited by
9 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献