Leveraging CO2 laser cutting for enhancing fused deposition modeling (FDM) 3D printed PETG parts through postprocessing

Author:

Sabri Hashem1,Mehrabi Omid23ORCID,Khoran Mohammad3,Moradi Mahmoud4

Affiliation:

1. Department of Mechanical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Tehran, Iran

2. Department of Mechanical Engineering, University of Birjand, Birjand, Iran

3. Department of Mechanical Engineering, Esfarayen University of Technology, Esfarayen, North Khorasan, Iran

4. Faculty of Arts, Science and Technology, University of Northampton, Northampton, UK

Abstract

In this study, the experimental investigation of the laser cutting process of polyethylene terephthalate glycol (PETG) sheets fabricated by the fused deposition modeling (FDM), was studied. The PETG sheets, with dimensions of 50 × 100 mm and thicknesses of 2.5, 5, and 7.5 mm, were fabricated using the FDM technique. Then, postprocessing laser cutting of the PETG sheets was undertaken by utilizing a 120-watt CO2 laser cutting. Response surface methodology was used to evaluate the influence of laser power (75–105 W), sheet thickness (2.5–7.5 mm), and cutting speed (4–10 mm/s) on the upper kerf width (UKW), lower kerf width (LKW), the ratio of UKW to LKW (ratio), and upper heat affected zone (HAZ) of the cutting kerf wall. The kerf wall was photographed byusing an optical microscope; and the kerf geometry dimension values were measured by ImageJ software. The results showed that all three parameters of sheet thickness, cutting speed, and laser power have impact on the kerf geometry characteristics. The reduction in the cutting speed and rise in the laser power increased the UKW and LKW, due to the increase in laser input heat. Furthermore, by increasing the sheet thickness and laser power and decreasing the cutting speed, the ratio decreased. Considering the minimum speed of 4 mm/s and maximum power of 105 W in the PETG sheet with a thickness of 7.5 mm, the highest values of the UKW and LKW were 336.6 and 582.2 μm, respectively. The HAZ decreased as power was reduced and speed was increased. The minimum HAZ value of 118 μm was achieved at a maximum speed of 10 mm/s with a sheet thickness of 7.5 mm.

Publisher

SAGE Publications

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3