A Study of the Micropore Structure of Carbonized Rayon Yarn by Nitrogen Adsorption and Nonane Pre-Adsorption

Abstract

Adsorption isotherms of nitrogen have been determined at 77 K on three samples of carbonized rayon yarn, both before and after the pre-adsorption of n-nonane. In their original state the three samples were all highly microporous. Application of the αs-method of isotherm analysis reveals that their micropore volumes were 0·17–0·19 cm3g−1 and their external surface areas 20–27 m2g−1 (the corresponding BET areas being 427–483 m2g−1). Nonane pre-adsorption resulted in blockage of the entire micropore structure only in the case of one sample: micropore volumes ∼0·1 cm3g−1 were still available for nitrogen adsorption in the other two samples. It appears that nitrogen molecules were able to gain access to some parts of these micropore structures through wider pore entrances which were not completely blocked by the pre-adsorbed nonane. The work has shown that the nonane pre-adsorption method requires further investigation before it can be used with confidence for the assessment of microporosity.