The effects of mechanical activation on corrosion resistance of cordierite ceramics-Reference-Cited by-同舟云学术

The effects of mechanical activation on corrosion resistance of cordierite ceramics

Published:2023-12-29 Issue:2 Volume:5 Page:83-88
ISSN:2687-6698
Container-title:Turkish Journal of Analytical Chemistry
language:
Short-container-title:

Author:

KESKİN Can Serkan¹^ORCID,AYNA ÇAKIR Ceren²^ORCID,ALTUNDAĞ Hüseyin¹^ORCID,TOPLAN Nil³^ORCID,TOPLAN Hüseyin Özkan³^ORCID

Affiliation:

1. SAKARYA ÜNİVERSİTESİ, FEN-EDEBİYAT FAKÜLTESİ

2. SAKARYA ÜNİVERSİTESİ, FEN BİLİMLERİ ENSTİTÜSÜ

3. SAKARYA ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, METALURJİ VE MALZEME MÜHENDİSLİĞİ BÖLÜMÜ, METALURJİ MÜHENDİSLİĞİ PR.

Abstract

The corrosion degrees of produced non-activated and activated cordierite-based ceramics were investigated in hydrochloric and sulfuric acid solutions. The composition of talc, alumina, and kaolinite powders was mechanically activated in a planetary mill. The concentrations of aluminum, magnesium, silicon, calcium, and potassium leached to the acid solutions from non-activated and activated cordierites were measured using ICP-OES. The amorphization of the structures was examined by XRD analysis. As a result, it has been determined that activated cordierite-based ceramics are more durable, and sulfuric acid solution causes more corrosion than hydrochloric acid.

Funder

Sakarya Üniversitesi

Publisher

Turkish Journal of Analytical Chemistry.

Subject

General Medicine

Reference26 articles.

1. C. N. Obradovic, N. Dordevic, S. Filipovic, N. Nikolic, D. Kosanovic, M. Mitric, S. Markovic, V. Pavlovic, Influence of mechanochemical activation on the sintering of cordierite ceramics in the presence of Bi2O3 as a functional additive, Powder Technol, 218, 2012, 157–161. https://doi.org/10.1016/j.powtec.2011.12.012.

2. J. Liao, G. Qing, B. Zhao, Phase equilibria studies in the CaO-MgO-Al2O3-SiO2 system with Al2O3/SiO2 weight ratio of 0.4, Metals, 13(224), 2023, 2-26. https://doi.org/10.3390/met13020224.

3. W. N. Obradović, V. Pavlović, M. Kachlik, K. Maca, D. Olćan, A. Đorđević, A. Thantshapanyan, B. Vlahović, V. Pavlović, Processing and properties of dense cordierite ceramics obtained through solid-state reaction and pressure-less sintering, Adv Appl Ceram, 118(5), 2019, 241–248. https://doi.org/10.1080/17436753.2018.1548150.

4. S. Yürüyen, N. Toplan, K. Yıldız, H. Ö. Toplan, The non-isothermal kinetics of cordierite formation in mechanically activated talc–kaolinite–alumina ceramics system, J Therm Anal Calorim, 125(2), 2016, 803–808. https://doi.org/10.1007/s10973-016-5277-1.

5. C. Başaran, N. Canikoğlu, H. Ö. Toplan, N. Toplan, The crystallization kinetics of the MgO–Al2O3–SiO2–TiO2 glass ceramics system produced from industrial waste, J Therm Anal Calorim, 125(2), 2016, 695–701. https://doi.org/10.1007/s10973-015-5139-2.