CRACKING AND EXFOLIATION OF TiO2 FILM IRRADIATED WITH EXCIMER LASER

Abstract

TiO 2 film deposited on glass was irradiated in air with single-shot KrF excimer laser pulse. The surface roughened as the result of the laser ablation. It is further noted that single-pulse irradiation with fluence ranging from 400 to 1200 mJ/cm2 gave rise to protrusion of the irradiated surface above the original surface, which is in contrast to usual expectation that irradiated surface is below the unirradiated surface. The surface protrusion is mainly attributed to the effect of surface tension. At the laser fluence of 1000 mJ/cm2, cracks were formed in the irradiated area and severe film exfoliation was observed at the periphery of the irradiated area due to the release of internal stress. With higher laser fluence above 1000 mJ/cm2, patches of film were observed to peel off within the irradiated areas. Hydrodynamic ablation is proposed to account for film exfoliation. The observed phenomenon is useful for further understanding how TiO 2 film reacts to strong UV laser irradiation.