Affiliation:
1. School of Mechanical Engineering, Taizhou University, Taizhou 318000, P. R. China
Abstract
The oxidation tests of electrospark deposited Ni -based coatings without and with 2.5 wt.% La 2 O 3 were conducted at 960°C in air for 100 h. The oxidation kinetic of the coatings was studied by testing the weight gain. The phase structures and morphologies of the oxidized coatings were investigated by XRD and SEM. The experimental results show that the coatings with 2.5 wt.% La 2 O 3 exhibits excellent high-temperature oxidation resistance including low oxidation rate and improved spallation resistance, due to the formation of a denser and more adherent oxide scale compared with that without La 2 O 3. The effects of La 2 O 3 on the oxidation resistance include the following two aspects: First, refinement of the coating grains promotes the selective oxidation of Cr , leading to the formation of protective chromia scale in a short time, and second, refinement of the oxide grains enhances the high-temperature creep rate, resulting in decrease of inner stress and improvement of spallation resistance of the oxide layer.
Publisher
World Scientific Pub Co Pte Lt
Subject
Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces,Condensed Matter Physics
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献