Affiliation:
1. College of Chemistry and Materials Science, Langfang Normal University, Langfang, P. R. China
Abstract
In this paper, CoO[Formula: see text]Co2P composite nanocatalysts as highly active catalysts were successfully prepared for catalytic hydrolysis of sodium borohydride (NaBH[Formula: see text] to generate hydrogen. For catalyst preparation, pre-synthesized Co(OH)2 nanosheets were uniformly mixed with sodium hypophosphite (NaH2PO[Formula: see text] and then treated through vapor-phase phosphorization process. For characterization, field-emission scanning electron microscopy (FE-SEM), energy dispersive spectrometry (EDS), X-ray diffraction (XRD), N2 adsorption–desorption measurement and X-ray photoelectric spectroscopy (XPS) were carried out, and traditional water-displacement method was performed to measure the hydrogen generation rate (HGR). It was found that component and catalytic activity of the composites were greatly affected by the ratio of Co(OH)2 to NaH2PO2. When the ratio was 2:1, the obtained catalyst composed of CoO and Co2P presented the highest HGR up to 3.94[Formula: see text]L min[Formula: see text] g[Formula: see text] using a 2[Formula: see text]wt.% NaBH[Formula: see text][Formula: see text]wt.% NaOH solution at [Formula: see text]C, and the apparent activation energy was detected as low as 27.4[Formula: see text]kJ mol[Formula: see text]. Additionally, the optimum CoO[Formula: see text]Co2P catalyst still retains 60% of the initial activity after recycling four times.
Funder
the Research Project of Hebei Education Department
Natural Science Foundation of Hebei Provence
Fundamental Research Funds for the Universities in Hebei Province
Publisher
World Scientific Pub Co Pte Lt
Subject
General Materials Science
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献