Nucleation, crystal growth, XRD, optical, electrical, PC, SEM, SHG and Z-scan analysis of LHPP for NLO and optical limiting application

Abstract

High-quality organic L-histidinium 4-nitrophenolate 4-nitrophenol (LHPP) single crystals were grown using an aqueous solution. The crystals were grown using slow evaporation solution technique (SEST) at a temperature of 40°C using a constant temperature bath (CTB). Nucleation growth rates were monitored for various durations using an optical microscope. The crystalline perfection was confirmed through sharp, high-intensity diffraction peaks observed in the theoretical and experimental powder X-ray diffraction (PXRD) analysis, which also confirmed the monoclinic crystal structure with the noncentrosymmetric P21 space group. The crystallite size and strain were calculated using Williamson–Hall coefficient. Vibrational frequency assignments of LHPP were determined using FTIR spectroscopic analysis. Optical properties were studied using UV–Vis NIR spectroscopic studies, which showed that the crystals have very low absorption and high transmittance in the entire visible region. Additionally, the optical energy bandgap (Eg) was calculated and found to be 6.15[Formula: see text]eV. Luminescence properties were studied using fluorescence (FL) analysis. Dielectric investigations were subjected to varying frequencies to study the suitability of the crystal for transistor application. The positive photoconductive (PC) nature of the crystal was confirmed using photoconductivity studies to confirm suitability for photodetector devices that measure the intensity of light rays. Etching studies revealed the growth pattern and the formation of different kinds of etch pits. The surface morphology was studied using scanning electron microscopy (SEM) and electrochemical studies were also carried out. The relative second harmonic generation (SHG) efficiency of the material was also examined and found to be 1.34 times that of standard KDP. The optical limiting and higher-order nonlinear optical (NLO) properties of the grown crystals were studied by the [Formula: see text]-scan method using a Nd: YAG laser functioning at 532[Formula: see text]nm.