ALUMINIZING OIL CASING STEEL N80 BY A LOW-TEMPERATURE PACK PROCESSING MODIFIED WITH ZINC ADDITION

Abstract

Different aluminide coatings were prepared on oil casing steel N80 at a relatively lower temperature of 530°C for 2 h by pack powder modified with different content of zinc (Zn). The cross-sectional microstructure, element distribution and properties of as-aluminized oil casing steel N80 were investigated by SEM, EDS, micro-hardness test and electrochemical corrosion measurement. Results show that aluminide coating with around 50 μm in thickness can be successfully achieved by a low-temperature pack aluminizing processing with the addition of Zn . Zn in the pack powder can enhance the uniformity and continuity of the coating layer, while it has little effect on the thickness of as-packed coating with the increasing content of Zn from 38.8 wt.% to 84.4 wt.%. As the content of Zn is over 58.8 wt.%, two layer coating consisting of pure Zn layer and Fe–Al aluminide layer can be formed on oil casing steel N80 substrate. Furthermore, oil casing steel N80 with aluminizing coating shows a higher microhardness than that of original one except in the depth range of pure Zn layer, but the microhardness of oil casing steel substrate does not decrease after aluminizing which can be inferred that low-temperature aluminizing processing reported here will not bring any damages on the mechanical properties of oil casing steel N80 . Additionally, a lower self-corrosion current density of oil casing steel N80 with aluminizing coating also indicates that low-temperature aluminizing processing is helpful to the corrosion resistance of oil casing steel N80 .