Effect of heat treatment on microstructure and wear resistance of high manganese steel surfacing layer

Abstract

The high manganese steel surfacing layer was deposited on Q235 steel by flux-cored wire gas shielded welding. The as-welded surfacing layer was heated at 1050[Formula: see text]C and quenched in the water, then was tempered at 300[Formula: see text]C. The microstructure, hardness and wear resistance of as-welded surfacing layer and that after heat treatment were comparatively analyzed. The results showed that compared with the as-welded surfacing layer, a large number of fine carbides dispersed in the austenite matrix for the surfacing layer after heat treatment. Meanwhile, the hardness and wear resistance of surfacing layer were slightly improved. The furrow in the abrasive wear for surfacing layer was shallower. Under the action of work hardening, the hardness of high manganese steel surfacing layer gradually increased while the loss weight decreased with the wear time less than 30 min. The hardness of surfacing layer reached the maximum and the loss weight of wear remained unchanged when the wear time was 30–60 min.