Comparison of warm laser shock peening and laser shock peening techniques in lengthening the fatigue life of welded joints made of aluminum alloy-Reference-Cited by-同舟云学术

Comparison of warm laser shock peening and laser shock peening techniques in lengthening the fatigue life of welded joints made of aluminum alloy

Published:2017-07-26 Issue:16-19 Volume:31 Page:1744045
ISSN:0217-9792
Container-title:International Journal of Modern Physics B
language:en
Short-container-title:Int. J. Mod. Phys. B

Author:

Su Chun¹²,Zhou Jianzhong¹,Meng Xiankai¹,Sheng Jie¹

Affiliation:

1. School of Mechanical Engineering, Jiangsu University, Zhenjiang, Jiangsu, P. R. China

2. School of Mechanical and Vehicle Engineering, Changzhou Institute of Technology, Changzhou, Jiangsu, P. R. China

Abstract

Welded joints made of 6061-T6 Al alloy were studied to evaluate warm laser shock peening (WLSP) and laser shock peening (LSP) processes. The estimation model of laser-induced surface residual stress was examined by means of experiments and numerical analysis. The high-cycle fatigue lives of welded joint specimens treated with WLSP and LSP were estimated by conducting tensile fatigue tests. The fatigue fracture mechanisms of these specimens are studied by surface integrity and fracture surface tests. Experimental results and analysis indicated that the fatigue life of the specimens processed by WLSP was higher than that with LSP. The large increase in fatigue life appeared to be the result of the larger residual stress, more uniform microstructure refinement and the lower surface roughness of the WLSP specimens.

Publisher

World Scientific Pub Co Pte Lt

Subject

Condensed Matter Physics,Statistical and Nonlinear Physics

Link

https://www.worldscientific.com/doi/pdf/10.1142/S0217979217440453

Reference7 articles.

1. Laser Peening Process and Its Impact on Materials Properties in Comparison with Shot Peening and Ultrasonic Impact Peening

2. A comprehensive investigation on the effects of laser and shot peening on fatigue crack growth in friction stir welded AA 2195 joints

3. Stability of residual stresses created by shot peening of pearlitic steel and their influence on fatigue behaviour

4. Nucleation of highly dense nanoscale precipitates based on warm laser shock peening

5. ANALYSIS OF SURFACE ROUGHNESS AT OVERLAPPING LASER SHOCK PEENING

Cited by 6 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Research on the transient forming process and high-temperature stability mechanism of warm laser shock imprinting;Optics and Lasers in Engineering;2021-11

2. Improving high cycle fatigue performance of gas tungsten arc welded Ti6Al4V titanium alloy by warm laser shock peening;International Journal of Fatigue;2021-08

3. Effect of rolling process on fatigue performance of stir zone of AA6061‐T6 doube‐side friction stir welding joint;Fatigue & Fracture of Engineering Materials & Structures;2020-11-30

4. The New Technologies Developed from Laser Shock Processing;Materials;2020-03-23

5. Surface roughness control of LY2 aluminum alloy milled surface subjected to laser shock wave planishing processing;Applied Surface Science;2019-08