Influence of Free Nitrogen on Creep Crack Growth of C-Mn Steel

Abstract

Different chemical compositions and heat-treatments of the C-Mn steels were investigated to characterise a susceptibility to cracking on cold bent tube. The C-Mn steels were categorised in terms of the content of free nitrogen. Ultimate tensile strengths, yield strengths and elongations were measured from the tensile testing at ambient, 250°C and 360°C. Significant increase in ultimate tensile strength and decrease in elongation were observed in high free nitrogen material at 250°C the temperature at which free nitrogen is most active. The lower ductility of the high free nitrogen material has provided higher susceptibility to cracking in the creep crack growth tests at 360°C. Cracking in the high free nitrogen material A was approximately three times faster than the low free nitrogen material C at the same C* value. The creep cracking and rupture life in the high free nitrogen materials were more sensitive to the material condition, for example, pre-straining and/or heat treatment because of the role of the free nitrogen in the steels.