Structure and Properties of Graphite-Molybdenum Brazed Joints

Abstract

The paper presents the results of X-ray microspectral studies of dissimilar brazed joints of molybdenum with graphite. It is shown that during active brazing of graphite with molybdenum, mutual diffusion processes occur, and the adhesion-active brazing filler metals penetrates into graphite, and interacts with it, which leads to the formation of carbide phases. When using the Ti-Cr-V and Cu-Ti-Ni systems brazing filler metals, titanium carbides are formed. The zirconium carbides are formed, when using the brazing filler metals based on the Zr-Pd(Mo) systems and the CxMey(Mo, Cr) carbides  are formed using the brazing filler metals of the Pd-Ni-Cr-Ge system. The results of tests for three-point bending showed that the using of Pd-Ni-Cr-Ge brazing filler metals provides stable strength at the level of 34-37 MPa, destruction occurs along graphite.