Application of chamfered narrow face mold technology to reduce longitudinal surface crack defects of hyperperitectic steel generated during flexible thin slab casting process-Reference-Cited by-同舟云学术

Application of chamfered narrow face mold technology to reduce longitudinal surface crack defects of hyperperitectic steel generated during flexible thin slab casting process

Published:2017 Issue:4 Volume:114 Page:413
ISSN:2271-3646
Container-title:Metallurgical Research & Technology
language:
Short-container-title:Metall. Res. Technol.

Author:

Zong Nanfu,Liu Yang,Zhang Hui

Publisher

EDP Sciences

Subject

Materials Chemistry,Metals and Alloys,Mechanics of Materials,Computational Mechanics

Link

http://www.metallurgical-research.org/10.1051/metal/2017030/pdf

Reference21 articles.

1. Influence of hot working on internal cracks in continuously-cast steel billets

2. Empowerment with knowledge— toward the intelligent mold for the continuous casting of steel billets

3. Analysis of Solidification Cracking Using the Specific Crack Susceptibility.

4. Learning about the nucleation pathway of MgO·Al2O3 spinel from an Fe–O–Al–Mg melt using a two-step nucleation mechanism

Cited by 18 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. A novel cooling structure of narrow copper plate for small chamfered mold;Ironmaking & Steelmaking: Processes, Products and Applications;2024-09-12

2. Effect of Mold Cooling Intensity on the Depression-Type Crack Formation and Mold Flux Infiltration During Continuous Casting Process;Metallurgical and Materials Transactions B;2023-09-15

3. Influence of Internal Cracking on Carbide Precipitation in Continuous Casting Bloom Induced by Soft Reduction Technology and the Resulting Segregated Band in Hot-Rolled Wire Rods;Archives of Metallurgy and Materials;2023-07-26

4. Application of a chamfer technology to overcome bulging deformation of slab narrow side during mechanical reduction process;The International Journal of Advanced Manufacturing Technology;2022-06-20

5. Design of Process and Equipment for Wide-Thick Slab CSC-Roll Reduction and Study of the Resulting Surface Crack Risk;Metallurgical and Materials Transactions B;2022-06-16