Influence of Surface Machining on Development of Stress Corrosion Cracking of Distribution Wheels of Main Circulation Pump in Nuclear Power Plants

Abstract

The present work deals with the causes of the damage to the distribution wheel of the main circulation pump of the nuclear power plant. During the solution of the problem, a significant influence of the final machining on the formation of cracks was found. Coarse surface machining can cause strain-induced martensite on the distribution wheel surface. Small pitting, which was observed on the surface of the distribution wheel, can be caused by the presence of martensite with less corrosion resistance. Thermal stress and residual stress after coarse final surface machining caused the growth of the cracks which initiated from the pitting.