Semi-Solid Deformation Behavior, Flow Stress Prediction and Deformed Microstructure of GH3536 Superalloy

Abstract

In current work, the deformation behavior and deformed microstructures of GH3536 superalloy in semi-solid state were investigated, and the semi-solid flow stress was predicted by artificial neural network (ANN) model. The semi-solid compression deformation was carried out at 1320-1350 °C, and the solid deformation behavior at 1200 °C was tested for comparison. The peak stress under 0.01-1 s-1 semi-solid deformation was 45.6-161.9 MPa. The peak stress decreased with the increase of deformation temperature and the decrease of strain rate. The ANN model could well describe semi-solid flow stress. During semi-solid deformation, the apparent viscosity dropped as shear rate increased. At high temperature and low strain rate, more liquid phase was distributed at grain boundaries. The solid grains coarsened as deformation temperature increased.