Fabrication of Zinc Ferrite (ZnFe<sub>2</sub>O<sub>4</sub>) by Sonochemical Methods: Physical and Magnetic Properties in Various Temperatures

Author:

Puspitasari Poppy1,Utomo Tri Agung Setyo1,Permanasari Avita Ayu2

Affiliation:

1. State of Malang University

2. Universitas Negeri Malang

Abstract

This study aims to determine the magnetic properties and structural properties of zinc ferrite (ZnFe2O4) material with the sonochemichal synthesis method. The sonochemichal method was obtained by sonication lasting for 30 minutes with the addition of 100 ml of 10 M NaOH. ZnFe2O4 material was sintered with temperature variations of 950°C, 1050°C, and 1150°C with a holding time of 2 hours. Phase identification revealed that the cubic phase structure of zinc ferrite is franklinite and also obtained crystal size results with values ​​of 70.58 – 84.71 nm. Morphological identification revealed that the ZnFe2O4 material had an irregular cubic shape and the highest agglomeration was at ZnFe2O4 temperature of 950°C. Identification of functional groups using FTIR characterization resulted in the wavelength range of 400-600cm-1 having basic lattices of Fe-O and Zn-O which occupy tetrahedral and octahedral positions, respectively. Magnetic identification uses VSM characterization which results that the sample is softmagnetic and gets several Mr, Ms, and Hc values. ZnFe2O4 with a sintering temperature of 1150°C in this study has the potential to be used as a microwave device.

Publisher

Trans Tech Publications, Ltd.

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3