Abstract
The growth of cracks in base steel P91 of 9Cr-1Mo class and in intercritical layer of HAZ is measured under creep coditions. For long term tests, a material degradation was detected consisting in an increase of crack growth rate and in a decrease of crack initiation time. An attempt is made to connect these effects with drop in ductility during thermomechanicalexposition.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference7 articles.
1. H. K. D. H. Bhadeshia: ISIJ International Vol. 41 (2001), p.626.
2. S. T. Kimmins, D. J. Smith: Jour. of Strain Analysis Vol. 33 (1998), p.195.
3. K. Laha, K S. Chandravathi, K. Bhanu Sankara Rao, S. L. Mannan, D. H. Sastry: Trans. Indian Inst. Met. Vol. 53 (2000), p.217.
4. H. Riedel: Fracture at high temperatures (Springer-Verlag, Germany, 1987).
5. J. Balík, M. Janeček: Kovove Mater. Vol. 40 (2002), p.307.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献
1. Sickness Risk in Personal Injury Insurance;Hokengakuzasshi (JOURNAL of INSURANCE SCIENCE);2015