Abstract
Alkali-activated slags represent an alternative to ordinary Portland cement due to reducing the environmental impact of the building industry. In spite of the numerous advantages of alkali activated slag mortars, alkali-activated aluminosilicates have big disadvantage – high value of shrinkage followed by formation of microcracks. This effect is caused by both autogenous and drying shrinkage and it finally results in volume contraction, microcracking and deterioration of the mechanical fracture properties. Therefore, using various types of polymer admixtures can overcome these problems. The aim of this paper is to present the effect of shrinkage-reducing admixture Peramin® SRA 40, polymer polyethylene glycol 1000 and polypropylene glycol on shrinkage and mechanical fracture characteristics of alkali-activated slag mortars. These admixtures were used in amount 0–2.0% weight of slag. The results showed that with increasing content of admixtures compressive and flexural strength decreased. Fracture tests with acoustic emission activity during this testing were carried out. Addition of 2% Peramin® SRA decreased shrinkage by 55%, but with 1% of Peramin® SRA the shrinkage was reduced only by 10%. Specimen with 1% of Peramin® is the most durable material, but more brittle compared to specimens with 1 and 2% of polypropylene glycol.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献