Affiliation:
1. Chulalongkorn University
2. Maharaj Nakorn Si Thammarat Hospital
3. University of Hong Kong
Abstract
The aim was to investigate the relation between micromorphology of porosity and electrical resistance of dental luting cements. Five dental luting cements were evaluated: zinc phosphate, glass ionomer, and three types of resin luting cements. Porosity of the specimen was analyzed by micro-CT and electrical resistance of cement was measured at voltage of 125 V up to 30 days and solubility of each specimen was calculated. It showed that the resin luting cements provided the highest electrical resistance regardless of amount of porosity. Zinc phosphate and glass ionomer had high porosity and the lowest resistance (14 and 3 kΩ, respectively). It was found that the electrical resistance of luting cement was not directly affected by the amount of porosity, but it seems to be related to pore connection. There is no correlation between electrical resistance and percentage of porosity but the morphology of porosity may have an influence on the electrical property of luting cement. Models of pore connection were proposed to explain the electrical resistance of luting cement.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference11 articles.
1. D.A. Gerdolle, E. Mortier, B. Jacquot, M.M. Panighi, Water sorption and water solubility of current luting cements: an in vitro study, Quintessence Int. 39e (2008) 107-114.
2. J. de la Macorra, G. Pradíes, Conventional and adhesive luting cements, Clin Oral Investig. 6 (2002) 198-204.
3. W. Tay, M. Braden, Dielectric properties of glass ionomer cements, J Dent Res. 60 (1981) 1311-1314.
4. C. Villat, X.V. Tran, N. Pradelle-Plasse, P. Ponthiaux, F. Wenger, B. Grosgogeat, et al, Impedance methodology: A new way to characterize the setting reaction of dental cements, Dent Mater, 26 (2010) 1127-1132.
5. N. Pradelle-Plasse, F. Wenger, B. Picard, P. Colon, Evaluation of microleakage of composite resin restorations by an electrochemical technique: the impedance methodology, Dent Mater, 20 (200) 425-434.