Abstract
Pressureless sintering of hexagonal boron nitride (BN) with and without additives was performed using a powder which was previously nitrided at 900oC and then heat treated at 1400oC. Sintering additives were B2O3 (2, 4, 6 wt %) and Y2O3 (2, 4, 6 wt %) and sintering temperatures was 1900oC. Sintered samples were characterized by XRD, SEM, micro hardness, density and mercury porosimeter measurements. Maximum density values of samples were 1.56 g/cm3 without additives and 1.63 g/cm3 with additives. Hardness values of samples were found to improve with the presence of additives.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference23 articles.
1. K. Niedenzu: Boron- Nitrogen Compounds, (Academic Pres. Inc., Springer Verlag, 1965), pp.147-153.
2. R. J. Brotherton: Progress in Boron Chemistry, (Vol. 2, Pergamon Press, California, 1970), pp.211-311.
3. Gmelins Handbook of Inorganic Chemistry, Boron Compounds BN Special Issue, (8th edition, Springer Verlag, 1988), pp.1-89.
4. A. Lipp, K. A. Shwetz and K. Hunold: J. of European Cer. Soc. Vol. 5 (1989), pp.3-9.
5. M. Hubacek. and M. Uekı: J. of Solid State Chemistry Vol. 123 (1996), pp.215-222.
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献