Mechanical properties of thermomechanically fabricated D03 Fe-33Al and B2 Fe-38Al intermetallic alloys containing Zr were investigated by means of tensile test and microhardness measurement. The Zr-added ternary alloys showed fine-grained microstructure containing large (Fe,Al)12Zr τ1 phase particles, while the binary alloy showed a single-phase microstructure consisted of coarse recrystallized grains. By introducing the large τ1 phase particles to Fe-Al matrix, tensile strength at room temperature as well as at high temperature (873K) was enhanced but tensile ductility at both temperatures decreased. On the other hand, it was found that vacancy hardening which was significant in the alloys with high contents of Al (i.e., Fe-38Al) was reduced by the large τ1 phase particles.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference11 articles.
1. C.G. McKamey: in: Physical Metallurgy and Processing of Intermetallic compounds, edited by N.S. Stoloff and V.K. Sikka: Chapman & Hall, New York, (1996).
2. D. J. Gaydosh, S. L. Draper, R. D. Noebe and M. V. Nathal: Mater. Sci. Eng. A Vol. 150 (1992), p.7.
3. F. Stein, M. Palm and G. Sauthoff: Intermetallics Vol. 2005 (2005), p.1275.
4. N. Matsumoto, Y. Kaneno and T. Takasugi: Tetsu-to-Hagané Vol. 93 (2007), p.400.
5. F. Stein, G. Sauthoff and M. Palm: Z Metallkd. Vol. 95 (2004), p.469.
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献