Dense mesoporous alumina bulks were successfully synthesized by a hydrothermal hot-pressing (HHP) method for mesoporous alumina powders prepared as starting material with a high BET surface area and narrow pore size distribution. As a result, mesoporous alumina HHP bulks had high density with uniformity pore size distribution and a high specific surface area. Their microstructural features for dense mesoporous alumina bulks were observed by SEM. The characterization of mesopores was examined.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference13 articles.
1. C. Misra, Industrial Alumina Chemicals, ACS Monograph 184, American Chemical Society, Washington, DC (1986).
2. F. Schüth and K. Unger In: G. Ertl, H. Knözinger and J. Weitkamp, Editors, Preparation of Solid Catalysts, Wiley-VCH, Weinheim (1999), p.77–80.
3. J. Cejka, Organized mesoporous alumina : synthesis, structure and potential in catalysis, Appl. Catal. 254 (2003) 327–338.
4. Z. Zhang, T.J. Pinnavaia, Mesostructured γ-Al2O3 with a Lathlike Framework Morphology, J. Am. Chem. Soc. 124 (2002) 12294–12301.
5. B. Tian, X. Liu, B. Tu, C. Yu, J. Fan, L. Wang, S. Xie, G.D. Stucky and D. Zhao, Self-adjusted synthesis of ordered stable mesoporous minerals by acid–base pairs, Nature Mater. 3 (2003) 159–163.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献
1. Cold sintering of ceramics and glasses: A review;Current Opinion in Solid State and Materials Science;2020-02