Abstract
Present work focusses on the effect of stress relaxation on the tensile behaviour of two commercially pure titanium alloys of different strength levels (Grade 1 and Grade 4) subjected to tensile tests at room temperature. The stress relaxation tests were performed by interrupting the tensile tests at regular strain intervals of 5% in the plastic region of the tensile curve and compared to the monotonic tensile tests at different strain rates ranging from 10-4to 10-1s-1. To understand the effect of anisotropy, samples were taken along 0° and 90° to rolling direction (RD) for both the alloys. Improvement in ductility of different levels at all the strain rates was observed in both the alloys when stress relaxation steps were introduced as compared to monotonic tests. However there is not much change in the flow stress as well as in strain hardening behaviour of the alloys. The true stress-true strain curves of Grade 4 samples taken in 90° to RD exhibited discontinuous yielding phenomenon after the yield point, which is termed as a yield-point elongation (YPE). The improvement in ductility of the Cp-Ti alloys can be linked to recovery process occurring during the stress relaxation steps which resulted in the improvement in ductility after repeated interrupted tensile tests. The paper presents and summarise the results based on the stress relaxation for the two different alloys.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference15 articles.
1. D. Banabic, Sheet Metal Forming: Processes Constitutive Modelling and Numerical Simulation, Springer Verlag Berlin Heidelberg, (2010).
2. H. Yamashita, H. Ueno, H. Nakai and T. Higaki, Honda R& D Technical., 24 (2012) 150-156.
3. K. Hariharan, O. Majidi, C. Kim, M. G. Lee and F. Barlat, Key Eng. Mater., 554-557 (2013)145-150.
4. K. Hariharan, O. Majidi, C. Kim, M. G. Lee and F. Barlat, Mater. Design, 52 (2013) 284-288.
5. H. D. Chandle, Mater. Sci. Eng., A 506 (2009) 130-134.
Cited by
18 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献