Effect of Resin Particle on Interfacial Shear Strength of CF/MAPP after Immersion

Author:

Hara Tomoaki1,Katogi Hideaki1,Takemura Kenichi1

Affiliation:

1. Kanagawa University

Abstract

Authors have reported that interfacial shear strength of Carbon Fiber (CF)/Maleic Anhydride grafted PolyPropylene (MAPP) was decreased by immersion for four weeks. As next stage, the purpose of this study is improvement of interfacial shear strength of CF/MAPP after immersion by adding resin particles around fiber. CF and resin particles added CF (RCF) were used as reinforcement. The major axis length of ellipse of resin particles was less than 5μm. In water absorption test, CF/MAPP and RCF/MAPP were immersed in distilled water for four weeks at room temperature. Micro debonding tests of CF/MAPP and RCF/MAPP after immersion were conducted. Fracture morphology of interface between fiber and resin was observed by using scanning electron microscope. As a result, following conclusions are obtained. In case of immersion for four weeks, the interfacial shear strength of RCF/MAPP was greatly increased (70%) compared with that of CF/MAPP. From fracture morphology of RCF/MAPP after immersion, some resin particles on CF surface were found after micro debonding test. Therefore, interfacial shear strength of CF/MAPP after immersion was increased by the effect of resin particles on CF surface.

Publisher

Trans Tech Publications, Ltd.

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

Cited by 1 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3