Abstract
With preplaced Ti-8Al-1Mo-1V + BN powder mixtures, the Ti-base composite coatings with in-suit synthesis nano particulates were obtained by laser cladding on titanium alloy substrate. The microstructures, fracture morphology, phase composition and mechanical property were studied by SEM, XRD and micro-hardness tests. The results show that, there are two kinds of typical nano particulates in the composites, i.e. the TiB with a diameter of ~400nm and the Ti2N with a diameter of ~10 nm. Both the TiB and Ti2N reinforced particulates are uniformly distributed in the composites. As a result, the average hardness of the composites were ~360HV0.05 which is about 20% higher than the substrate. In the composites, the distribution of Ti2N particulates shows a peculiar characteristic of dendrite-like morphologies. The analysis shows that the Ti2N precipitates out from the solid state α-Ti(N) is the reason why Ti2N is only of a diameter of ~10nm and distributes in a certain way of dendrite-like morphologies.
Publisher
Trans Tech Publications, Ltd.
Reference11 articles.
1. L. Geng, D.R. Ni and Z.Z. Zheng: Acta Materiae Compositae Sinica Vol. 23 (2006), p.1 (In Chinese).
2. L.F. Chen, Y. Liu, H.P. Tang, H.Y. Liu and Y.P. Huang: Rare Metal Materials and Engineering Vol. 34 (2005), p.1609 (In Chinese).
3. D.E. Alman and J. A Hawk: Wear Vol. 225 (1999), p.629.
4. P.A. Xiao, X.H. Qu, C.M. Lei, B.J. Zhu, M.L. Qin and P.Y. Huang: Materials Science and Engineering of Powder Metallargy Vol. 6 (2001), p.279 (In Chinese).
5. S. Gorsse, J.P. Chaminade and Y. Le-Petitcorps: Composites Part A: Applied Science and Manufacturing Vol. 29 (1998), p.1229.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献