Abstract
SiCp/A356 composites containing 20% (volume fraction) SiC and three kinds of different filler metals were investigated by vacuum brazing process. Brazability of SiCp/A356 composites was analyzed after nickel plating on the surface of composites and without nickel plating process. The effects of holding time on microstructure of the brazed joints of SiCp/A356 composite were studied by metallographic microscope, SEM and Energy spectrum analysis. The results showed that nickel plating on the surface of composite contributed to improve brazability of SiCp/A356 composites prominently, while inferior brazability displayed without nickel plating on the surface of composites. Hardness of joints brazed at holding time of 6 min, 8 min and 10 min were studied, consequently the hardness of the weld seam region is the highest when the holding time was 8 min.
Publisher
Trans Tech Publications, Ltd.
Reference7 articles.
1. Wu Mao, Chang Lingling, Investigation of Al-based Alloys for Brazing SiCp/Al Composites, Rare Metal Materials and Engineering. 40(2011) 132-135.
2. H. Uzun, Friction stir welding of SiC particulate reinforced AA2124 aluminium alloy matrix composite, Mater and Design, 28 (2007)1440-1446.
3. Bhushan RK, Kumar S, Das S. Effect of machining parameters on surface roughness and tool wear for 7075 Al alloy SiC composite. Int J Adv Manuf Technol, 50(2010) 459–669.
4. Huibin Xu, Bofang Zhou, Quanxiang Luo, Study on stirring brazing of SiCp/A356 composites with the Zn27Al filler alloy in air. Advanced Materials Research Vols. 383-390 (2012) 2710-2713.
5. Metin K, Wear behavior of plasma-sprayed Al-12Si/SiC composite coatings under dry and water-lubricated sliding. Int J Adv Manuf Technol 55 (2011) 911–920.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献