Affiliation:
1. Wuhan University of Science and Technology
Abstract
The silicon-boron(Si-B) pitch was successfully synthesized by solution-thermal treatment method using coal pitch, polycarbosilane and borane pyridine as starting materials. The B-Si pitch carbonization product was attained by carbonization in the temperature 900°C under flowing argon. The Si-B pitch prepared and its carbonization product were characterized by SEM, FT-IR, TG-DSC and XRD. The results show that the carbonization product has C-Si and C-B bonds and the silicon and boron components of the product is still amorphous when it is treated at 900°C. The weight loss of the Si-B pitch carbonization product at 900°C for 12h in air atmosphere is only 3.76wt%. The weight loss of the product is less than 4 wt% when the oxidation temperature reaches 1180°C. The prepared B-Si pitch carbonization product possesses good anti-oxidation property at high temperature in air atmosphere.
Publisher
Trans Tech Publications, Ltd.
Reference12 articles.
1. R.Y. Luo, Z. Yang and L.F. Li: Carbon, Vol. 38 (2000), p.2109.
2. C. Badini, P. Fino, A. Ortona and C. Amelio: J. Eur. Ceram. Soc., Vol. 22 (2002), p. (2071).
3. H.L. Li, H.J. Li, J.H. Lu, X. Zhang and K.Z. Li: Carbon, Vol. 49 (2011), p.1416.
4. X.H. Zhang, Y.G. Du, J.Y. Xiao, W.J. Zhang and L.C. Zhang: Appl. Surf. Sci., Vol. 255 (2009), p.4250.
5. M. Huang, K.Z. Li, K.J. Li, Q.G. Fu and G.D. Sun: Carbon, Vol. 45 (2007), p.1105.