Mechanical Test of Aluminum-Zirconium-Silicate Composite Prototype with Filler Volume Variation

Author:

Karlina Elin1,Usri Kosterman1,Febrida Renny1,Panatarani Camellia1,Joni I Made1,Fatmala Yunita1

Affiliation:

1. Universitas Padjadjaran

Abstract

Recently, ceramic material has become a main object of scientific interest especially in dental material. The advance of dental materials technology has led to use of zirconia-based ceramics for composite filler. In this study, composite filler has been synthesized from natural zircon sand through geopolymerization method. Composite prototype were made with different filler volume to evaluate mechanical properties including hardness number and diametral tensile strength. Samples divided into two groups with 50 wt% filler volume (group A) and 75 wt% filler volume (group B) which 3 samples for each group. The surface micro hardness of each group tested by Leco M-400-H1 vickers microhardness testing machine and for diametral tensile strength tested using universal testing machine (Lloyd) with crosshead speed of 1,0 ± 0,25 mm/min. The data were analyzed using independent sample t-test. The results showed that the average of hardness number on group A was 13,8 VHN while for group B was 24,1 VHN. The average of diametral tensile strength for group A was 20,461 MPa and 27,689 MPa for group B. Statistical result showed that the value (P<0,05). The conclusion, there is a signifficant difference on the result of hardness test between group A (50 wt% filler volume) and group B (75 wt% filler volume) and also on diametral tensile strength test.

Publisher

Trans Tech Publications, Ltd.

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3