The paper considers the technology of obtaining metal nanoparticles by the method of induction levitation. A bulk metal sample of titanium with a purity of 99.9% and a mass of 0.4 g, which was heated and held in a state of flux levitation by a high-frequency electromagnetic field, was used as the basic raw material for nanoparticles. The obtained nanoparticles were examined using Х-ray diffraction analysis to determine the purity of the product. The analysis showed that it is high. Particle size distribution was investigated using dynamic light scattering, where the average particle diameter is 55 and 47 nm, obtained in Ar and He, respectively. The morphology was studied using scanning electron microscopy, according to which the average diameter of the particles synthesized with He and Ar is 45 and 57 nm, respectively.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference10 articles.
1. A.V. Vorotyntsev, A.N. Petukhov, T. S. Sazanova, V.I. Pryakhina, A.V. Nyuchev, K.V. Otvagina, A.N. Markov, M.E. Atlaskina, I.V. Vorotyntsev, V.M. Vorotyntsev, Imidazolium-based SILLPs as organocatalysts in silane production: Synthesis, characterization and catalytic activity, Journal of Catalysis. 375 (2019) 427–440.
2. Ma. Kus, T. Y. Alic, C. Kirbiyik, C. Baslak, K.Kara and D. A. Kara, Synthesis of Nanoparticles, Micro and Nano Technologies. (2018) 392-429.
3. E.C. Okress, D.M. Wroughton, G. Comenetz, P.H. Brace, and J.C.R. Kelly, Electromagnetic Levitation of Solid and Molten Metals, Journal of Applied Physics. 23 (1952) 545.
4. S.I. Bakhtiyarov and D.A. Siginer, Electromagnetic Levitation Part I: Theoretical and Experimental Considerations, Tech Science Press. 5 (2008) 99-112.
5. S.I. Bakhtiyarov and D.A. Siginer, Electromagnetic Levitation Part III: Thermophysical Property Measurements in Microgravity, Tech Science Press. 4 (2009) 112.
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献