Abstract
In this work, a new microwave dielectric material for LTCC applications, xAl2O3+ (1-x) BaO-Al2O3-B2O3-SiO2-ZnO (x=0.3, 0.4, 0.5 and 0.6) glass-ceramics, was synthesized. The effect of Al2O3 on the microstructure, mechanical properties and electrical properties of BaO-Al2O3-ZnO-B2O3-SiO2 glass-ceramics was studied in this paper. The crystallinity was studied by jade6.5 software using the whole pattern fitting method. The XRD analysis showed that the content of BaAl2Si2O8 increased first and then decreased with the increase of Al2O3 content. It is found that the formation of phase BaAl2Si2O8 contributes to strong bending strength. The xAl2O3+ (1-x) BaO-Al2O3-SiO2-ZnO-B2O3 glass-ceramics sintered 2h at 920°C has the excellent microwave dielectric properties at x=0.4, εr=7.4, tanσ=1.49×10-3 at 13.5GHz, τf=-42.67ppm/°C, flexural strength= 184MPa.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference14 articles.
1. Qin T, Zhong C, Yang H, Qin Y, Zhang S 2019 Ceram. Int. 45 10899.
2. Chen Y, Li E, Duan S, Zhang S 2017 ACS Sustainable Chemistry & Engineering. 5 10606.
3. M.T. Sebastian, H. Jantunen 2008 Int. Mater. Rev. 53 57.
4. Li B, Li W, Zheng J 2017 J. Alloys Compd. 725 1091.
5. Sun T, Xiao H, Guo W, Hong X 2010 Ceram. Int. 36 821.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献