Eu3+ and Tb3+ ions singly activated Gd2O2S hollow spheres have been successfully synthesized via solvothermal method by using Gd (NO3)3, Eu (NO3)3, Tb (NO3)3 and thiourea as raw materials. Detailed characterization of the as-prepared samples were obtained by X-ray diffractometry (XRD), field emission scanning electron microscopy (FE-SEM), transmission electronic microscope (TEM) and photoluminescence (PL) spectroscopy. The results demonstrate that at 220 oC for 24 h, the molar ratio of thiourea/Gd3+ has no significant impact on the phase composition of Gd2O2S products. With the reaction time increased from 6 h to 24 h, the morphology of Gd2O2S samples changed from ellipsoidal to near-spheroidal structure, but still remained hollow structure. PL results show that the strongest emission peaks for Gd2O2S:Eu3+ and Gd2O2S:Tb3+ samples were centered at 625 nm and 545 nm, corresponding to the 5D0→7F2 transition of Eu3+ ions and 5D4→7F5 transition of Tb3+ ions, respectively. The quenching concentrations for Eu3+ and Tb3+ ions were 12% and 6%, which can be attributed to the exchange interaction for Eu3+ and Tb3+ ions, respectively.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference25 articles.
1. Y.P. Du, Y.W. Zhang, L.D. Sun and C.H. Yan: Atomically Efficient Synthesis of Self-assembled Monodisperse and Ultrathin Lanthanide Oxychloride Nanoplates, J. Am. Chem. Soc., Vol. 131 (2009), p.3162.
2. B.W Zhang, H.F. Zou, H.G. Guan, Y.Z. Dai, Y.D. Song, X.Q. Zhou and Y. Sheng: Lu2O2S: Tb3+, Eu3+ nanorods: luminescence, energy transfer, and multicolour tuneable emission, Cryst. Eng. Comm., Vol. 18 (2016), p.1.
3. F. Liu, J.B. Lian, N.C. Wu, J. He, X. Zhang and F. Liu: One-step solvothermal synthesis, a worm-shaped morphology and luminescence properties of green-emitting Y2O2S:Tb3+ nanophosphors, Opt and Laser Technol., Vol. 99 (2018), p.167.
4. J.B. Lian, F. Liu, P. Liang, J.M. Ren and F. Liu: Synthesis of Gd2O2S:Eu3+ hollow sphere by a hydrothermal method assisting with reduction route, J. Ceram. Process. Res., Vol. 17 (2016), p.752.
5. B.C. Liu, Q. Wang, S.L. Yu, T. Zhao, J.X. Han P. Jing, W.T. Hu, L.X. Liu, J. Zhang, L.D. Sun , C.H. Yan, H. Ren, L.Y. Zhang, T.T. Wang, L. Li, Z. Su and C.G. Wang: Double shelled hollow nanospheres with dual noble metal nanoparticle encapsulation for enhanced catalytic application, Chem. Commun., Vol. 49 (2013), p.6036.
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献