Numerical Simulation of Physical-Mechanical Properties Based on the Composition of GTAW Weld Metal Alloys with Dissimilar Base Metals

Abstract

Dissimilar weld-metal joints in aluminum alloys 5083 and 6061-T6 are often found in aircraft, railroad structures, ships, bridges, oil platforms, and building structures. However, welding of dissimilar metals is relatively more difficult due to the different metallurgy and thermophysical properties of the two alloys. The purpose of this study is to evaluate the physical-mechanical properties of the Tungsten Arc Welding (GTAW) process through numerical simulations of different welded joints between the 5083 and 6061-T6 aluminum alloys. The GTAW welding simulation process is carried out by 300 x 100 x 3 mm plate butt joints along 300 mm. GTAW weld metal is prepared for tensile test samples and metal alloy composition, the test is observed in the base metal and welded area. The results of the chemical composition test of the weld metal obtained that the composition is close to Al 5083 base metal so that the mechanical properties of the weld metal tend to be identical with Al 5083 alloy. The results of numerical simulation on the mechanical properties of GTAW weld metal at temperature conditions of 25 to 700 °C obtained several things, including 1) the range of thermal conductivity decreased from 174.393 to 86.424 W/mK. 2) The density increased from 2,348 to 2,663 gr/cm3. 3), the young modulus appears to decrease from 68,667 to 0 GPa. 4) the shear modulus decreases from 25,724 to 0 GPa. 5) the type of heat increases from 0.904 to 17,306 J/gK, and 6) the Poisson ratio increased from 0.335 to 0.5.