Abstract
Simulated Heat Affected Zone (HAZ) samples of TP347H stainless steel welded joint with 800-1380°C peak temperature thermal cycles were produced using Gleeble 3180 thermal mechanical simulator. 600°C constant speed tensile tests for simulated HAZ samples were carried out, and the precipitates of the simulated samples were analyzed by EDAX. The results show that the lowest Reduction of Area (RoA) was around 53% - 56% in 900-1150°C, which was about 15% lower than the maximum RoA in 800-1380°C. The reasons for decrease of HAZ high temperature plasticity were related to the precipitation of NbC. The fine NbC precipitated in the crystal and grain boundary enhanced strength of grain at high temperature, which resulted plastic deformation or slip at high temperature were mainly concentrated in the grain boundary, and high temperature plasticity of HAZ were decreased.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference7 articles.
1. John C. Lippold, Damian J. Kotecki. Welding Metallurgy and Weldability of Stainless Steels. John Wiley &Sons, Inc. (2005).
2. O. Yoo, Y.J. Oh, B.S. Lee, et al. The effect of the carbon and nitrogen contents on the fracture toughness of Type 347 austenitic stainless steels. Materials Science and Engineering: A, 405, 147-157. (2005).
3. Irvine K J,Murray J D and Pickering F B. The effect of heat-treatment and microstructure on the high-temperature ductility of 18%Cr-12Ni-1Nb steels. Journal of the Iron and Steel Institute, 10: 166-179. (1960).
4. Chen Zhongbing, Gao Miaomiao. Xie Xiaoyuan, et al. Fracture Behaviors of TP347H Steel Welded Joint under Elevated Temperature and High Stress. Welding Technology, 48 (9): 118-121. (2019).
5. Erneman J,Schwind M,Andren H,et al. The evolution of primary and secondary Niobium Carbonitrides in AISI 347 stainless steel during manufacturing and long-term ageing. Acta Materialia, 54 (1): 67-76. (2006).
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献